Technical Data

Everlube® 690

MIL Spec, MoS2 Solid Film Lubricant

U.S.A. 1-800-428-7802 - 1-770-261-4800 Europe 44 (0) 1386 421444 www.everlubeproducts.com

Product Description

Everlube 690 is a thermally cured MoS2 based solid film lubricant which utilizes a high molecular weight phenolic binder system. This coating was primarily developed to prevent galling and seizing for fasteners and fastening related applications. It is recommended for use with self-locking fasteners. Specifications for this product can be found at: http://www.everlubeproducts.com/products

Features / Benefits

•               Excellent coefficient of friction

•               Prevents galling and seizing

•              Very good chemical resistance

•               Ideal for higher load carrying applications

Markets

Typical Applications

•              Fasteners

•               Industrial Machinery

•               Fabricated Metal Parts

•              Mechanical Components

•              Small to medium fasteners

•              Guides, slides and tracks

•              Threaded connectors and disconnects

•               Bearings, gears, splines and cams

Physical Properties

Lubricating Solid Binder

Color and Appearance* Carrier

Solids (by weight)*

Density*

Flash Point

Volatile Organic Compound Theoretical Coverage1 Alternative or Repair Coatings

MoS2

High molecular weight phenolic Matte grey finish Solvent Borne 41% to 43%

9.6 土 0.5 lb/gal (1150 土 60 grams/liter)

21°F (-6°C)

660 grams/liter (5.5 lb/gal)

552 ft2/gal @ 0.5 mils (13.5 m2/liter @ 12.7 microns)

For touch-up applications, Perma-Slik G or Lubri-Bond 220 works well with Everlube 690.

Processing Information

Dry Film Thickness Dilution/Cleanup Solvent Dilution Ratio (for spray)

Cure Cycle

Suggested Pretreatment Suggested Application Methods

0.2 to 0.7 mils (5 to 18 microns)

MEK or 50% Ethyl Alcohol and 50% Toluene (preblended) 1:3 (Product to Solvent by volume) Adjust as needed 1 hr @ 300°F± 15°F (149°C ± 10°C) Part metal temp)

Grit Blast and/or Phosphate Dip Spin / Spray

For additional information, please see Processing Bulletin # 3000-A


Everlube 690, MoS2 Solid Film Lubricant Page 2 of 2______


Typical Functional Properties


Corrosion Resistance*

ASTM Test Method

Value

Test Panel

ASTM B117

>100 hrs. @ 5% Neutral Salt Spray

Test Panel Coating Method

 

0.5 mil on grit blasted steel panel

Abrasion Resistance

ASTM D4060

Good

Coefficient of Friction

ASTM D2714

.04 to .06

Operating Temperature Range

 

-100。to 325°F (-73。to 163°C)

Load Carrying Capacity*

ASTM 2625, Method B

> 200,000 psi

Wear Life*

ASTM 2625, Method A

> 60 minutes

Chemical Resistance (ASTM D-2510, Method C)


Isopropyl Alcohol or Ethyl Alcohol

Pass

Diethanolamine

Pass

Mineral Spirits or Paint Thinner

Pass

Hydrochloric Acid (10%)

Pass

Toluene

Pass

Sodium Hydroxide (10%)

Pass

Acetone

Pass

Distilled Water

Pass

Skydrol 500 (room temp)

Pass

Jet Fuels (JP-4)

Pass

Hydraulic Fluids

Pass

Trichloroethylene:

Pass

Anti-Icing Fluids

Pass

 

 

Note: Chemical resistance may vary depending on the cure cycle. N/R = Not recommended Additional Information


Shelf Life and Storage:

One year from date of shipment, stored in a factory sealed container between the temperatures, 40°F to 100°F.

Coatings are thermally stable, but we do not recommend prolonged exposure outside of the specified temperature range listed above.

Packaging:

Everlube 690 is available in Gallons, 5-gallon pails, and quarts Warranty:

No representation of warranty is expressed or implied and all warranties including warranties of marketability and fitness for use are expressly disclaimed. Nothing herein shall be construed as permission or recommendation to practice a patented invention without a license.


分享到:


联系我们
常州复诺纳米科技有限公司
地址:江苏省常州市武进区常武中路801号
电话:0519-88709957
手机:13813588407
电邮:1948751975@qq.com


版权信息